RENOFORM 1665/1

Home > Products > Product Review > Metalforming Lubricants > RENOFORM 1665/1 >


Product Review

	Engine and Gear Oils

	Mould Release Agents

	Metalworking Fluids

	Metalforming Lubricants

		RENOFORM VB 360

		RENOFORM MBO 236

		RENOFORM HBO 962/2

		RENOFORM FW Series

		RENOFORM 702-461-AV

		RENOFORM 569

		RENOFORM 519-HT

		RENOFORM 51-DO

		RENOFORM 457

		RENOFORM 319-IS

		RENOFORM 1665/1

		TRENOIL S Series

		TRENOIL T Series

		TRENOIL SP Series


	Corrosion Preventives

	Quenching Oils

	Greases

	Industrial Lubricants

	Rapidly Biodegradable Lubricants

	Other products and services



Publication

Exhibitions

FUCHS for REACH - The new EU chemical law

EURO PI

RENOFORM 1665/1

Cold forming lubricant

RENOFORM 1665/1 is an extreme pressure lubricant suitable for a wide variety of cold forming operations on difficult ferrous and non-ferrous alloys. RENOFORM 1665/1 provides a lubrication system which maximizes tool life by reducing friction and eliminating metal pick-up on dies and punches. Residual films are easily cleaned in conventional cleaning systems.

Benefits of using RENOFORM 1665/1

Provides EP lubrication to prevent metal pick-up on tooling
Suitable for a wide variety of cold forming operations
Is recommended as lubricant for bar and wire drawing of high tensile steels
Easily cleaned in most conventional cleaning systems
Non hazardous to use - contains no toxic ingredients

Application:

Can be applied directly to the wire or rod on small one and two die headers. Should be flowed directly on the dies and punches on large headers or parts formers. Usually use as supplied. Can be diluted with blending oil for less difficult operations.

Typical Physical & Chemical Characteristics

Properties	Unit	Value	Norm Test
Density at 15 °C	Kg/l	0.970	ASTM D 1298
Colour		>8.0	ASTM D 1500
Viscosity at 40 °C	mm²/s	100	ASTM D 445
Flash point COC	°C	202	ASTM D 92
Copper corrosion / 3 h - 20 °C	degree of corr.	3 a	ASTM D 130
Copper corrosion / 24 h - 20 °C	degree of corr.	4 b	ASTM D 130
Copper corrosion / 3 h - 50 °C	degree of corr.	4 a	ASTM D 130
Copper corrosion / 24 h - 50 °C	degree of corr.	4 b	ASTM D 130
Copper corrosion / 3 h - 100 °C	degree of corr.	4 a	ASTM D 130
Copper corrosion / 24 h - 100 °C	degree of corr.	4 c	ASTM D 130
Four ball test / welding load	N	6000	ASTM D 2783
Reichert wear test	mm²	3.7	FLP*

FLP* = FUCHS Laboratory Procedure

Disclaimer of Liability