ANTICORIT RP4107 S

Home > Products > Product Review > Corrosion Preventives > ANTICORIT RP4107 S >


Product Review

	Engine and Gear Oils

	Mould Release Agents

	Metalworking Fluids

	Metalforming Lubricants

	Corrosion Preventives

		ANTICORIT RP4107 S

		ANTICORIT PL3802 LV

		ANTICORIT OHK

		ANTICORIT MKR

		ANTICORIT DFW

		ANTICORIT DFO

		ANTICORIT DF

		ANTICORIT BW 366

		ANTICORIT 6120/42

		ANTICORIT 5012 S

		ANTICORIT 03 W-C


	Quenching Oils

	Greases

	Industrial Lubricants

	Rapidly Biodegradable Lubricants

	Other products and services



Publication

Exhibitions

FUCHS for REACH - The new EU chemical law

EURO PI

ANTICORIT RP4107 S

Corrosion Protection Oil

ANTICORIT RP 4107 S is a barium-free corrosion preventive which offers cold rolled steel excellent protection in condensation, salt spray and open shed conditions.

ANTICORIT RP 4107 S has good drawing properties and is also easily removed with neutral or alkaline water-based cleaners.

ANTICORIT RP 4107 S is thixotropic and provides optimum film stability on vertical surfaces.

ANTICORIT RP 4107 S meets VW A 001, Mercedes-Benz DBL 6747.15 and Opel B 040 1270 specifications and is correspondingly recommended.

ANTICORIT RP 4107 S protects semi-finished cold rolled steel components during transportation and open sheds storage when good protection and easy removability are priorities. Also the standard corrosion preventive used by the European steel industry.

Application:

ANTICORIT RP 4107 S can be applied by dipping, spraying or rolling.
ANTICORIT RP 4107 S is normally applied electrostatically to cold rolled steel. ANTICORIT RP 4107 S is approved by DUMA and Peabody. When electrostatically spraying or filtering, the temperature should not fall below 40 °C.
As with all thixotropic products, light settling can occur after longer periods of storage.
If sealed in the original container, ANTICORIT RP 4107 S can be stored for min. 5 years at 5-40 °C.

Characteristics:

Properties	Unit	Value	Test method
Odour		mild
Colour		4.0, turbid	ASTM D 1500
Density at 15 °C	kg/l	0.887	ASTM D 1298
Viscosity at 20 °C	mm²/s	145	ASTM D 445
Viscosity at 40 °C	mm²/s	36	ASTM D 445
Flashpoint	°C	214	ASTM D 92
Pourpoint	°C	+3	ASTM D 97
Film weight	g/m²	13.5	FLP-F 3 *)
Run-off		OK	E 14 **)
Removability		OK	VW 52.02
Oxide ash	% mass	1.4	DIN EN ISO 6245
Neutralization number	mgKOH/g	0.2	ASTM D 974
Saponification number	mgKOH/g	5.6	ASTM D 94
Solid impurities	% mass	< 0.05	DIN 51 592
Water content	% mass	< 0.2	DIN 51 777-2
Aromatic content of the base oil	% mass	< 10	VM Test method TML 1 ***)
Corrosion Protection Data (on RRSt. 1405 m test panels)
Humidity cabinet	hours	196	ASTM D 1748
Condensation climate	cycles	> 20	DIN 51 386-1
Salt spray test	hours	24	ASTM B 117

*)	= FUCHS Laboratory procedure
**)	= Adam Opel AG test method
***)	= Vauxhall Motors Limited, England

Disclaimer of Liability