ANTICORIT PL3802 LV

Home > Products > Product Review > Corrosion Preventives > ANTICORIT PL3802 LV >


Product Review

	Engine and Gear Oils

	Mould Release Agents

	Metalworking Fluids

	Metalforming Lubricants

	Corrosion Preventives

		ANTICORIT RP4107 S

		ANTICORIT PL3802 LV

		ANTICORIT OHK

		ANTICORIT MKR

		ANTICORIT DFW

		ANTICORIT DFO

		ANTICORIT DF

		ANTICORIT BW 366

		ANTICORIT 6120/42

		ANTICORIT 5012 S

		ANTICORIT 03 W-C


	Quenching Oils

	Greases

	Industrial Lubricants

	Rapidly Biodegradable Lubricants

	Other products and services



Publication

Exhibitions

FUCHS for REACH - The new EU chemical law

EURO PI

ANTICORIT PL3802 LV

Corrosion Protection Oil, Prelube

Low-viscosity, barium-free corrosion prevention oil with very good drawing properties offering excellent protection for sensitive cold rolled steel in condensation, open shed and acidic conditions. Easily removed with neutral or alkaline water-based cleaners. Excellent film stability on vertical surfaces
compared to conventional oils. The product is slightly turbid.

ANTICORIT PL 3802 LV is recommended for use in coil washing equipment for the cleaning and protection of cold rolled steel. If the film weight is in the region of 2 g/m², almost all subsequent pressing operations can be performed without any additional lubricants.

Application:

ANTICORIT PL 3802 LV can be applied by dipping, -spraying or rolling.
ANTICORIT PL 3802 LV is recommended for use in coil and panel washers. When filtering, the temperature should not fall below 40 °C.
As with all thixotropic products, light settling can occur after longer periods of storage.
If sealed in the original container, ANTICORIT PL 3802 LV can be stored for min. 5 years at 5-40 °C.

Characteristics:

Properties	Unit	Value	Test method
Odour		mild
Colour		4.0, turbid	ASTM D 1500
Density at 15 °C	kg/l	0.900	ASTM D 1298
Viscosity at 20 °C	mm²/s	155	ASTM D 445
Viscosity at 40 °C	mm²/s	16	ASTM D 445
Flashpoint	°C	150	ASTM D 92
Film weight	g/m²	5.5	FLP-F 3 *)
Run-off		OK	E 14 **)
Removability		OK	VW 52.02
Oxide ash	% mass	2.1	DIN EN ISO 6245
Solid impurities	% mass	< 0.05	DIN 51 592
Water content	% mass	< 0.2	DIN 51 777-2
Aromatic content of the base oil	% mass	< 10	VM Test method TML 1 ***)
Corrosion Protection Data (on RRSt. 1405 m test panels)
Condensation climate	cycles	> 15	DIN 51 386-1
Salt spray test	hours	24	ASTM B 117

*)	= FUCHS Laboratory procedure
**)	= Adam Opel AG test method
***)	= Vauxhall Motors Limited, England